Abstract
In this research, cvc fleece, nylon fleece and polyester as a sample, were subjected on saturated water absorption test, wicking rate test, diffusion area test, and saturated water drying rate test. there are eightteen cloth material in order to explore the effects of different cloth material or different denier on moisture absorption and drying rate. It found that water absorption test simple of 100% Polyester polar fleece (210g/yard) with brush and pilling have the best performance. The water absorption is 1051% in average, and the wicking rate test to sample of T75D with 100D brush fleece is a the best, The height of wicking rate test, way of the horizontal brush hair surface is 15.1cm, horizontal not brushed surface is 15.2cm in 10 minutes, and the height wicking rate test, way of the longitudinal brush hair surface is 14.4cm, longitudinal not brushed surface is 14.1cm. Testing of drying rate, the simpleof CVC brush fleece (480g/yard) was the best, the residual moisture content was 7.05% after 40 minute.
Keywords摘要
本研究針對cvc刷毛布、尼龍刷毛布及聚酯刷毛布分別進行飽和吸水試驗、蕊吸試驗、乾燥速率試驗以及飽和吸水乾燥速率試驗，實驗使用十八種布樣進行比較，分別以改變其布樣成分進行探討不同材質及丹尼數對於吸濕及乾燥速率的影響。由實驗數據得知，飽水試驗以100%Poly 單刷單搖(210 g/yard)的平均吸水率最為佳，其平均吸水率達1051%，而蕊吸試驗以T75D+T100D單刷 為最佳，其10分鐘橫向刷毛面蕊吸高度達15.1公分，橫向未刷毛面蕊吸高度達15.2公分，縱向刷毛面蕊吸達14.4公分，縱向未刷毛面蕊吸達14.1公分，飽和乾燥速率則CVC大絨刷毛布(480 g/yard為最佳)，第40分鐘的殘餘水分率為7.05%。
關鍵字Also in this issue
Full TOC →- Study of Blended TPU/ PA 6 Composite Electrospinning Nonwoven for Blocking Aerosol ParticlesI-Chen Yang, Ya-Xuan Chiu, Shuo-Qi Zeng, Yi-Jun Pan
- Celebration & DressPi Jing Ferng, Wen Kuei Lai
- Evaluation and Test of Sulfonation Upgrading Performance of PVA Proton Exchange MembraneWan-Ling Liao, Chih-Hung He, Mei-Feng Lai, Ching-Wen Lou, Jia-Horng Lin
- Flame Retardancy and Properties Evaluation of Polyurethane Foam by Adding AlginatePolyurethane Foam by Adding AlginateKai-Xiang Jiang, Ruei-Ren Ou, Chen-Hung Huang, Ching-Wen Lou, Jia-Horng Lin
- Far AwayWan-Chen Tu, Jing-Yun Fan