Preparation of Poly(butyl methacrylate) Fiber by Solution Blowing and Its Absorptive Performance to Oily Organic Compounds

溶液噴射製備聚甲基丙烯酸丁酯纖維及其油性有機物吸附性能

Y. Feng 封嚴 ✉ School of Textile Tianjin Polytechnic University
G. Y. Wang 王剛毅 School of Textile Tianjin Polytechnic University
X. P. Zhuang 莊旭品 School of Textile Tianjin Polytechnic University
Z. F. Zhang 張志飛 School of Textile Tianjin Polytechnic University

Abstract

Poly(butyl methacrylate) (PBMA) was synthesized by suspension polymerization. The spinning solution was prepared with hydroxyethyl methylacrylate(HEMA) as physical crosslinking agent, divinyl benzene(DVB) as chemical crosslinking agent and N, N - dimethyl acetamide as solvent. The PBMA fiber with composite crosslinking structure was made via solution blowing process and the influence of the crosslinking agent content on the fiber morphologies was discussed. The absorptive properties of the fiber to diesel oil, engine oil and soybean oil were also studied. The results showed that the fiber diameter was uniform when hot air temperature, extrusion rate, air pressure and suction wind volume was 170 ℃, 10 ml/h, 0.03 MPa and 2520 m3/h, respectively. For different oil absorption test, the saturated oil absorbency of the fiber to diesel oil, soybean oil and engine oil was 14g/g, 10g/g and 8g/g. Also the fiber presented good hydrophobic performance.

Keywords

摘要

採用懸浮聚合工藝製備聚甲基丙烯酸正丁酯（PBMA），以甲基丙烯酸β羥乙酯（HEMA）為物理交聯劑，二乙烯基苯（DVB）為化學交聯劑，N,N-二甲基乙醯胺（DMAc）為溶劑，製備紡絲溶液。採用溶液噴射法製備複合交聯結構PBMA纖維，研究了交聯劑含量及種類對纖維形貌和結構的影響，探討了PBMA纖維對柴油、機油與大豆油等油性有機物的吸附性能。結果表明，當熱空氣溫度為170℃，擠出速率為10ml/h，牽伸風壓為0.03MPa，抽吸風風量為2520m3/h時，所得纖維直徑均勻，形態良好。對不同油品的吸附性能測試結果表明，纖維對柴油、大豆油和機油的飽和吸附率分別為14g/g、10g/g和8g/g，且具有良好的拒水親油性。

關鍵字

Also in this issue

Full TOC →

Research Polyester Fabric Resistance Temperature Balance in Different Colors and Concentrations of Dye
Y. P. Chen, Y. N. Yu, J. M. Lee, W. H. Hsing
The study of biomass system polyamide fabric moisture management features
Kun-Shan Huang, Hsiao-Chi Tsai
Application of three dimensional woven fabric filters in a membrane bioreactor
Fang Zhao, Fangfang Weng, Gang Xue, Qiuran Jiang, Yiping Qiu
Design of Optimal Gabor Filter for Fabric Defect Detection
L. Tong, W. K. Wong
A Study of Taiwan's consumer lifestyle of vintage market - A hand to hand Marketplace as an example
I-chin Tsai, Yan-zhi Wei

Full text 全文

Abstract only

作者未授權開放全文下載。

Issue: Vol. 23 No. 4 (2016)
Section: Original Research Articles
Pages: 218-222
Submitted: 2016-06-12
Published: 2016-06-12
ID: JHGT-16-221
Views: 1
Downloads: 0

引用 How to cite

Feng, Y., Wang, G. Y., Zhuang, X. P., & Zhang, Z. F. (2016). Preparation of Poly(butyl methacrylate) Fiber by Solution Blowing and Its Absorptive Performance to Oily Organic Compounds. Journal of the Hwa Gang Textile, 23(4), 218-222. https://jhgt.org.tw/article/view/198

@article{feng2016_198,
  author  = {Feng, Y. and Wang, G. Y. and Zhuang, X. P. and Zhang, Z. F.},
  title   = {Preparation of Poly(butyl methacrylate) Fiber by Solution Blowing and Its Absorptive Performance to Oily Organic Compounds},
  journal = {Journal of the Hwa Gang Textile},
  year    = {2016},
  volume  = {23},
  number  = {4},
  pages   = {218--222},
  issn    = {1025-9678},
  url     = {https://jhgt.org.tw/article/view/198}
}

TY  - JOUR
AU  - Feng, Y.
AU  - Wang, G. Y.
AU  - Zhuang, X. P.
AU  - Zhang, Z. F.
TI  - Preparation of Poly(butyl methacrylate) Fiber by Solution Blowing and Its Absorptive Performance to Oily Organic Compounds
JO  - Journal of the Hwa Gang Textile
T2  - 華岡紡織期刊
VL  - 23
IS  - 4
PY  - 2016
SP  - 218
EP  - 222
KW  - Poly(butyl methacrylate)
KW  - Solution Blowing
KW  - Oily Organic Compound
SN  - 1025-9678
UR  - https://jhgt.org.tw/article/view/198
AB  - Poly(butyl methacrylate) (PBMA) was synthesized by suspension polymerization. The spinning solution was prepared with hydroxyethyl methylacrylate(HEMA) as physical crosslinking agent, divinyl benzene(DVB) as chemical crosslinking agent and N, N - dimethyl acetamide as solvent. The PBMA fiber with composite crosslinking structure was made via solution blowing process and the influence of the crosslinking agent content on the fiber morphologies was discussed. The absorptive properties of the fiber to diesel oil, engine oil and soybean oil were also studied. The results showed that the fiber diameter was uniform when hot air temperature, extrusion rate, air pressure and suction wind volume was 170 ℃, 10 ml/h, 0.03 MPa and 2520 m3/h, respectively. For different oil absorption test, the saturated oil absorbency of the fiber to diesel oil, soybean oil and engine oil was 14g/g, 10g/g and 8g/g. Also the fiber presented good hydrophobic performance.