Vol.28, No.2(2021-4)(117-123) 
Discussion on the dyeability of disperse yellow 241 dye in supercritical carbon dioxide
分散性黃色241染料於超臨界二氧化碳中染色性探討
J.C. Chang , H. Chen , W.C. Huang , S.M. Lin
張瑞哲、陳翰、黃文謙、林尚明
In this experiment, the C.I. disperse yellow 241 was dyed in supercritical CO2 with different pressures and temperatures to dye polyester fibers, and the apparent color strength value (K/S value) and dyeing fastness were discussed to find the best of the dyeing conditions. The results show that the dyeing temperature can be dyed at 70°C under the pressure of 3625psi, but its K/S value is the lowest, indicating that the dye has not entered the polyester fiber in the supercritical CO2, but as the temperature increases, the K / S value will rise. When dyeing at a temperature of 120℃, it can be dyed when the pressure is 2300 psi, and its K/S value is also low, which means that the dye dissolves less dye in supercritical CO2. As the pressure increases, the K/S value rises accordingly. Based on the above results, it is found that the best condition for dyeing C.I. disperse yellow 241 in supercritical CO2 is temperature 120°C and pressure 3625 psi.
本實驗以分散性黃色241染料於超臨界CO2中改變不同的壓力和溫度對聚酯纖維進行染色,並探討其表觀色力度值(K/S值)與染色堅牢度,進而找出最佳的染色條件。結果顯示在3625psi壓力下染色溫度於70°C時即可染著,但其K/S值較最低,表示染料在超臨界CO2中尚未進入聚酯纖維的內部,但隨著溫度升高時,K/S值便會隨之上升。在溫度120℃下染色時其壓力於2300 psi時就可染著,其K/S值也較低,表示染料在超臨界CO2中溶解較少染料,隨著壓力升高時,K/S值隨之上升;綜合以上結果發現分散性黃色241於超臨界CO2染色的最佳條件為溫度120°C 壓力3625 psi。
disperse, supercritical CO2, polyester fibers, dyeing
分散性、超臨界CO2、聚酯纖維、染色
Year Volume
2021 28.1 | 28.2
2020 27.1 | 27.2
27.3 | 27.4
27.5 | 27.6
27.7 |
2019 26.1 |
2018 25.1 |
2017 24.1 | 24.2
24.3 | 24.4
24.5 | 24.6
24.7 | 24.8
24.9 |
2016 23.1 | 23.2
23.3 | 23.4
23.5 | 23.6
23.7 | 23.8
2015 22.1 | 22.2
22.3 | 22.4
22.5 |
2014 21.1 | 21.2
21.3 |
2013 20.1 | 20.2
20.3 | 20.4
2012 19.1 | 19.2
19.3 | 19.4
2011 18.1 | 18.2
2010 17.4