Vol.28, No.1(2021-1)(41-47) 
Research different textiles of Lux and brightness with EL
冷光片搭配不同布樣之照度與明暗度研究
C.T Tsai Y.T Lin W. H. Hsing
蔡政廷 林雅庭 邢文灝
In this study, in the four colors of red polyester fabric, blue polyester fabric, green polyester fabric, and yellow polyester fabric, the L value will decrease as the concentration increases, and the LUX value will also decrease. It can be known that the L value of the red polyester cloth and the red polyester cloth plus the luminescent film are analyzed at different concentrations. When the concentration of the red polyester cloth is 0.1%, the L value is 51.43, and the red polyester cloth concentration is 2%. The L value was 44.6, the L value was 52.25 when the red polyester cloth plus luminescent sheet concentration was 0.1%, and the L value was 45.77 when the red polyester cloth plus luminescent sheet concentration was 2%. The L value of different concentrations of the yellow polyester cloth and the fluorescent yellow and the luminescent film were measured. The L value decreased with the increase in the concentration of the yellow polyester cloth from 0.1% to 2%. When the minimum concentration of the yellow polyester cloth is below 0.1% to 2%, the L value will decrease as the concentration increases, and the minimum concentration after the yellow polyester cloth and the fluorescent yellow and the cold light sheet are affixed is 0.1. From 2% to 2%, the L value decreases as the concentration increases.
本研究是以在紅色聚酯布、藍色聚酯布、綠色聚酯布、黃色聚酯布等四種顏色會隨著濃度上升,L值會隨之下降,LUX值也會隨之下降。可得知紅色聚酯布與紅色聚酯布加冷光片之不同濃度進行的L值分析,實驗得知紅色聚酯布濃度為0.1%時,L值為51.43,紅色聚酯布濃度為2%時,L值為44.6,紅色聚酯布加冷光片濃度為0.1%時,L值為52.25,紅色聚酯布加冷光片濃度為2%時,L值為45.77。並佐證黃色聚酯布和螢光黃與冷光片貼合後之不同濃度進行的L值分析,黃色聚酯布從濃度為0.1%至2%時,隨著濃度增加,L值會隨之下降,黃色聚酯布貼合冷光片後最低濃度為0.1%至2%時,隨著濃度增加,L值會隨之下降,黃色聚酯布與螢光黃與冷光片貼合後最低濃度為0.1%至2%時,隨著濃度增加,L值會隨之下降。
Electroluminescence, Lab value, brightness
冷光片、Lab值、亮度
Year Volume
2021 28.1 | 28.2
2020 27.1 | 27.2
27.3 | 27.4
27.5 | 27.6
27.7 |
2019 26.1 |
2018 25.1 |
2017 24.1 | 24.2
24.3 | 24.4
24.5 | 24.6
24.7 | 24.8
24.9 |
2016 23.1 | 23.2
23.3 | 23.4
23.5 | 23.6
23.7 | 23.8
2015 22.1 | 22.2
22.3 | 22.4
22.5 |
2014 21.1 | 21.2
21.3 |
2013 20.1 | 20.2
20.3 | 20.4
2012 19.1 | 19.2
19.3 | 19.4
2011 18.1 | 18.2
2010 17.4