Vol.24, No.9(2017-11)(603-607) 
Effect of various weight ratio of Thermoplastic Polyurethane on the Blending morphology and Thermal properties of impact-resistance Polypropylene
添加熱塑性聚氨酯對耐衝擊聚丙烯共混物之 共混型態與熱性質之影響
Ting-An Lin1, Ching-Wen Lou2,3,4, Jia-Horng Lin1,3,4,5,6
林庭安, 樓靜文, 林佳弘
This study aimed to investigate the effect of various weight ratio of thermoplastic polyurethane (TPU) on the blending morphology, melting behavior, crystalline behavior, and thermal properties of impact-resistance polypropylene (PP). From the test results, SEM images shown that the morphology of PP/TPU blends become rougher and the particle size of TPU with an increasing addition of TPU. DSC results revealed that the addition of TPU would cause the decreasing crystalline and melting enthalpy of PP, while would not significantly influence the crystalline and melting temperature. TGA results indicated that the increasing addition of TPU led to higher thermal degradation temperatures of PP/TPU blends in every step.
本研究以熔融混合法製備耐衝擊聚丙烯/熱塑性聚氨酯共混物,並研究不同重量比例之熱塑性聚氨酯對於耐衝擊聚丙烯之共混型態、熔融行為、結晶行為與熱性質之影響。SEM結果顯示,隨著熱塑性聚氨酯的比例提升,耐衝擊聚丙烯/熱塑性聚氨酯的斷面型態越粗糙,且TPU顆粒尺寸越大。DSC結果顯示,熱塑性聚氨酯的添加對於耐衝擊聚丙烯之結晶溫度與熔融溫度無顯著影響,但其對於耐衝擊聚丙烯之結晶焓與熔融焓之變化隨著比例提升而有所下降。 TGA結果顯示,隨著熱塑性聚氨酯之添加比例提升,四組耐衝擊聚丙烯/熱塑性聚氨酯共混物在三階段之熱裂解溫度皆有所提升。
Impact-Resistant Polypropylene, Thermoplastic Polyurethane, Blends, Thermogravimetric Analysis.
耐衝擊聚丙烯, 熱塑性聚氨酯, 共混物, 熱重分析
Year Volume
2021 28.1 | 28.2
2020 27.1 | 27.2
27.3 | 27.4
27.5 | 27.6
27.7 |
2019 26.1 |
2018 25.1 |
2017 24.1 | 24.2
24.3 | 24.4
24.5 | 24.6
24.7 | 24.8
24.9 |
2016 23.1 | 23.2
23.3 | 23.4
23.5 | 23.6
23.7 | 23.8
2015 22.1 | 22.2
22.3 | 22.4
22.5 |
2014 21.1 | 21.2
21.3 |
2013 20.1 | 20.2
20.3 | 20.4
2012 19.1 | 19.2
19.3 | 19.4
2011 18.1 | 18.2
2010 17.4