Study on the Cool Feeling of Nanofiber Films Prepared by Electrospining Method and Varies Polymer Blended with Different proportion of cooling powder/nano aluminum compound
不同比例涼爽礦石粉/奈米鋁化合物添加於高分子材料以靜電紡絲法製備奈米涼爽纖維膜之研究
C. C. Wang
黃柏瑀, 王權泉
In this study,various ratio of nano cooling powder/nano-aluminum compound were added into polymers (polyacrylonitrile(PAN),polyamide(Nylon) and Polyester(PET)) prepared cool nano-fiber membrane by electrospinning method,The viscosity of spinning solutions and cool feeling values(Q-max) of nano-fiber membrane were researched. From experimental results found the viscosity increased with the increase of ratio nano-aluminum compound. In addition, a scanning electron microscopy will be used to observed fineness in the fiber. This research discovers that increasing of the proportion of nano-aluminum compound will increase the fineness of fiber. Above all, the nano-aluminum compound shown significant effect on Q-max. The Q-max values of Nylon nano fiber membrane up to 0.164 W/cm2, were better than PAN and PET at any ratio of cooling additives。
本研究以改變涼爽礦石粉末/奈米鋁化合物比例加入不同高分子聚合體(Nylon、PAN、PET)溶液中均勻分散,以靜電紡絲法製備奈米涼感纖維膜,觀察改變涼爽礦石粉末/奈米鋁化合物比例對涼感的影響,並經由電子顯微鏡觀察表面與纖維細度。由研究中觀察,改變涼爽礦石粉末/奈米鋁化合物比例會使黏度上升,纖維細度變大,細度範圍在0.18-0.68μm之間。當鋁化合物佔添加的總比例越多瞬間涼感值越佳,Nylon的奈米涼爽纖維膜在涼爽礦石粉末/奈米鋁化合物添加比例0/3的情況下,瞬間涼感值可達0.164 W/cm2,其瞬間涼感值較同比例下的PAN、PET效果優異。
Electrospinning, Cool Jade, Nano-Aluminum Compound, Polymer, Cool Feeling
高分子聚合體、靜電紡絲、涼爽礦石粉末、奈米鋁化合物、瞬間涼感
Year Volume
2020 27.1 | 27.2
27.3 |
2019 26.1 |
2018 25.1 |
2017 24.1 | 24.2
24.3 | 24.4
24.5 | 24.6
24.7 | 24.8
24.9 |
2016 23.1 | 23.2
23.3 | 23.4
23.5 | 23.6
23.7 | 23.8
2015 22.1 | 22.2
22.3 | 22.4
22.5 |
2014 21.1 | 21.2
21.3 |
2013 20.1 | 20.2
20.3 | 20.4
2012 19.1 | 19.2
19.3 | 19.4
2011 18.1 | 18.2
2010 17.4