Mechanical Properties and Fire Performance of Basalt Fiber Reinforced Phenolic Resin Composites
玄武岩纖維/酚醛樹脂複合材料力學及防火性能之研究
C. P. Chin, K. C. Lee, Y. J. Pan*
秦治平, 李貴琪, 潘毅鈞
In this study, filament-wound basalt fiber reinforced phenolic resin composites prepreg were made, and then, manual fibers were stacked and laminated in parallel, and thermoforming, production of basalt fiber reinforced phenolic resin composite . Focuses on fiber content of the composite tensile strength, limiting oxygen index, carbide layer area, the impact on the back of temperature. It was found that when the basalt fiber content rises, the better tensile mechanical properties, fire performance has declined.
本研究以纏繞成型法製作玄武岩纖維複合材料預浸材,再以手排疊法將纖維以平行的方式進行疊層,並熱壓成型,製作玄武岩纖維/酚醛樹脂複合板材,主要探討纖維含有率對複合材料拉伸強力、限氧指數(LOI值)、碳化層面積、背面溫度的影響。結果發現,當玄武岩纖維含有率上升時,其拉伸力學性質愈佳,防火性能卻下降。
basalt fiber, phenolic resin, limiting oxygen index, carbide layer area, the back of temperature
玄武岩纖維、酚醛樹脂、LOI值、碳化層面積、背面溫度
Year Volume
2020 27.1 | 27.2
27.3 |
2019 26.1 |
2018 25.1 |
2017 24.1 | 24.2
24.3 | 24.4
24.5 | 24.6
24.7 | 24.8
24.9 |
2016 23.1 | 23.2
23.3 | 23.4
23.5 | 23.6
23.7 | 23.8
2015 22.1 | 22.2
22.3 | 22.4
22.5 |
2014 21.1 | 21.2
21.3 |
2013 20.1 | 20.2
20.3 | 20.4
2012 19.1 | 19.2
19.3 | 19.4
2011 18.1 | 18.2
2010 17.4