The Analysis of Absorbing Electromagnetic Waves used by Swelling Method and Electroless Nickel Plated Way on Polyester Fiber
聚酯織物以膨潤處理方式經無電極鍍鎳對電磁波吸收效果之分析
K. C. Lee, H. J. Yu*, H. J. Chang
李貴琪, 游輝仁, 張紘瑞
The research is using Electroless nickel plating way to make Polyester Fiber’s surface cover with metal. By use the different parts of temperature that it‘s at 40℃, 50℃, 60℃, and 70℃, and with the different parts of time to 5, 10, 15, 20, 25 minutes. Then observe how the plating temperature and plating time effect on the absorption of electromagnetic wave. As the increase of plating time and temperature, the nickel layers became more. The surface resistance is relatively lower. At this experiment when the temperature is at 70℃, plating the Polyester Fiber after 25 minutes, the absorption of electromagnetic wave could reach 33dB. The electromagnetic wave absorption bandwidth rates can get up to 53%.
本研究是將聚酯纖維使用無電極鍍鎳的方法,使在聚酯纖維表面鍍上鎳金屬層,並藉由電鍍溫度40℃、50℃、60℃、70℃、80℃,與電鍍時間5分鐘、10分鐘、15分鐘、20分鐘、25分鐘,觀察其電鍍溫度與電鍍時間對電磁波吸收值的影響。隨著電鍍時間、溫度的增加鍍上之鎳鍍層越多,表面電阻值相對越低,本實驗在無電極鍍鎳溫度為80℃,電鍍20分鐘時電磁波吸收值可達34dB,其電磁波吸收頻寬率可達53%之最佳條件。
electroless nickel plated, electromagnetic wave absorber, PET fabric
無電極鍍鎳、電磁波吸收、聚酯織物
Year Volume
2020 27.1 | 27.2
27.3 |
2019 26.1 |
2018 25.1 |
2017 24.1 | 24.2
24.3 | 24.4
24.5 | 24.6
24.7 | 24.8
24.9 |
2016 23.1 | 23.2
23.3 | 23.4
23.5 | 23.6
23.7 | 23.8
2015 22.1 | 22.2
22.3 | 22.4
22.5 |
2014 21.1 | 21.2
21.3 |
2013 20.1 | 20.2
20.3 | 20.4
2012 19.1 | 19.2
19.3 | 19.4
2011 18.1 | 18.2
2010 17.4